Method and apparatus for pressing particleboard

ABSTRACT

The invention relates to a method for pressing particleboard whereby steam under pressure is introduced into the particleboard mat during pressing. The invention provides for reduced press time, improved particleboard quality and makes practical greater board thickness. The apparatus comprises a pair of platens having apertures and associated conduits for steam and exhaust, and means for enclosing the mat while steam is being injected. Steam is introduced into one platen and exhausted through the other.

[ June 24, 1975 METHOD AND APPARATUS FOR PRESSING PARTICLEBOARD 3,6l9,450 ll/l97l Futo 264/109 Primary Examiner-Robert F. White [75} Inventor: Kuo-Cheng Shen, Ottawa, Canada I I ASSISIQNI ExammerJ. R. Hall [73] Asslgnee: Canadlan Patents & Development Au e A or Fi R ld G, Bimer Limited, Ottawa, Canada [22] Filed: Nov. 10, 1972 57 S C PP 305,531 The invention relates to a method for pressing particleboard whereby steam under pressure is introduced [52] us CL H 264/101, 264/120. 264/122 into the particleboard mat during pressing. The inven- 51 Int. c|.'-' .1 B 29J 5/00 Pmvides for reduced Press impmved [58] Field of Search H 264/109 120 82 I22 cleboard quality and makes practical greater board M thickness. The apparatus comprises a pair of platens having apertures and associated conduits for steam [56] References Cited and exhaust, and means for enclosing the mat while steam is being injected. Steam is introduced into one UNlTED STATES PATENTS platen and exhausted through the other. 3,280.237 [0/1966 Corbin et al 264/l09 3354148 1 H1967 Haas et alv 264/!20 5 Claims, 4 Drawing Figures REG 23 2| 6 e 25 21 I I0 V A f f i2 22 REG J U l\\\ lK\\\\\\\ l\\\\\\ \\\\\\\\\\\\\Nl\\\\\\\\\N l V L L u 3 y 2 U T I I \/L \I\ \\\Y7 2 1816 ll t PATENTEU JUN 2 4 ms SHEET CONVENTlONAL 75 PROCESS U 5 4o E g U! m Li] I 20 STEAM PRESS PROCESS Io l l I I l l BOARD THICKNESS (INCHES) FIG.4

METHOD AND APPARATUS FOR PRESSING PARTICLEBOARD This invention relates to a method for pressing particleboard. and more particularly to a method and apparatus comprising the introduction of steam under pressure into the particleboard mat during the pressing thereof.

In the production of particleboard. a thermosetting adhesive binder is mixed with wood particles. a mat is formed and pressed. In conventional pressing the heat required to cure the adhesive binder is transferred predominately by conduction from the surfaces of the hot press platens and some time is required to raise the temperature at the center of the mat. With increasing mat thickness, press time does not vary linearly with board thickness but increases more rapidly.

In the classic steam shock or steam jet technique the surface layers of the mat are given a high moisture content, for example, by spraying with water. As the hot platens contact the surface layers of the mat the water vaporizes and moves towards the center of the mat. In this way the temperature of the core can be raised more quickly. This technique has the limitation that the amount of moisture must be optimumly balanced because the higher the moisture content, the faster the temperature rise, but also the longer the press time to eliminate the excess moisture which interferes with the curing of the adhesive binder and causes blisters. With this method there is also difficulty in applying water at the bottom surface of the mat because of the hot caul plate on which the mat is formed.

It has been proposed to reduce press time by passing low pressure steam through the mat from one edge to the other during conventional hot pressing. However, with this method it was found that the maximum temperature which could be reached in the center of the mat at the discharge side was 100C. The main drawbacks of this method are that temperatures and moisture gradients develop along the steam flow direction across the mat which would probably result in warping of a full size (4 X 8 foot) board, and that larger mats would require a longer time for the steam to pass through.

In the commercial production of particleboard. press time is the bottleneck on the production line and is the major factor in determining production efficiency. With increased board thickness production efficiency is decreased further. Another disadvantage of conventional pressed particleboard is that it is susceptible to thickness swelling when exposed to moisture unless treated after pressing.

It has been found that since a particleboard mat is normally porous in construction, it is possible to force steam under pressure through the mat by means of apertured press platens. The injected steam provides rapid heat transfer to the mat for rapid curing of the adhesive binder. Steam is injected through an apertured platen on one side of the mat and exhausted through another apertured platen on the opposite side of the mat. By confining the mat in a suitable chamber and restricting the exhaust, elevated temperatures and pressures can be maintained within the chamber to obtain both rapid cure of the adhesive binder and a relaxation of the compressive stresses placed on the wood particles when the mat is originally compressed to the desired board density. The steam can be rapidly released from the mat at the end of the cycle with the release of pressure from the chamber through the apertures in the platens.

In accordance with the present invention particleboard is pressed using a press including a pair of platens wherein each platen has apertures opening to one surface thereof which is adjacent to the other platen and chamber defining means enclosing the region between the platens. The process comprises pressing a mat comprising wood particles and a thermosetting adhesive binder between the platens, introducing steam under pressure into the mat through the apertures of one platen and exhausting the steam through the apertures of the other platen, restricting the exhaust rate to maintain an elevated pressure and temperature within the chamber for a time sufficient to cure the adhesive binder, and releasing the steam pressure from the chamber and separating the platens for removal of the particleboard.

Valves associated with the chamber and steam source provide means for pressurizing the chamber. controlling the steam flow through the mat and releasing the pressure from the chamber.

An object of this invention is to provide a method for pressing particleboard with shorter press time.

Another object is to provide for the making of particleboard having a thickness greater than has previously been practical or economical in a flat press process.

Another object is to provide particleboard which has improved characteristics particularly with respect to water absorption and thickness expansion.

Yet another object of this invention is to provide dimensional stabilization of the particleboard with the pressing operation.

The invention will be further described with reference to the drawings in which:

FIG. 1 is a schematic sectional view of the apparatus;

FIG. 2 is a sectional view taken at 2-2 of FIG. 1;

FIG. 3 shows an alternate embodiment of a portion of the apparatus;

FIG. 4 shows an example of the typical relationship between press time and board thickness for a conventional process and the steam-press process of the present invention.

Referring to FIG. 1 the apparatus comprises a pair of press platens l and 2 which are adapted to be moved relative to one another by suitable means (not shown). Between the platens l and 2 is an annular sealing frame 3 of the desired thickness, which rests on the lower platen 2. When the platens are pressed together against the sealing frame member 3, a sealed chamber 4 for the mat 5 is defined. The inner face of the platens have a plurality of apertures 6 and 7 interconnected with passageways 8 and 9, respectively, which communicate with a pressurized steam source through conduits l0 and ll. Inlet valves l2, l3, and 14 control the steam input. The passageways 8 and 9 also connect with conduits l5 and 16. Exhausting and release of steam pressure are controlled by valves 17 and 18.

Each platen includes passageway means 21 connected with conduits 22 to a source of a heating fluid, preferably also steam, which keeps the platens at the desired temperature.

In operation, the particleboard mat 5, preferably prepressed and contained by two screens 25 for ease of handling, is placed on the lower platen 2 within the sealing frame 3. The platens 1 and 2 are brought together relative to one another in sealing engagement with the frame member 3, defining a chamber 4. In order to raise the pressure within the chamber quickly steam inlet valves 12 and 13 are opened. while the outlet valves 17 and 18 remain closed. After the desired pressure is reached, the steam inlet valve 13 is closed and the outlet valve 18 is opened partially to allow steam to flow through the mat while maintaining the desired pressure in the chamber 4. After the desired steaming time the inlet valve 12 is closed and all exhaust valves are opened to release the steam pressure before the press is opened. During the above operation the temperature of the platens is controlled by the temperature of the heating fluid through the passageways 2]. The temperature of the platens is preferably 5 to F higher than that of the steam injected.

The apparatus of FIG. 1 also provides for changing the direction of steam flow. By correctly manipulating the inlet valves 12 and 13 and the outlet valves 17 and 18 the steam can be injected into the mat through the top or bottom platen 1 and 2 respectively. It was found that for thick boards, reversing the steam flow direction at some point during the steam injection operation, provides for more uniform and rapid heating of the mat.

In the alternate embodiment of FIG. 3, radial passageways 39 are used to facilitate varying the spacing of the apertures 37 radially from the center of the platen 32 to provide uniform steam flow to all portions of the mat. The density at the edges of a laterally unconfined mat will be lower hence the porosity of the mat in this region will be higher. Having more widely spaced apertures at the edges provides more uniform flow through all regions of the mat.

In the following examples the apparatus used was generally ofthe type shown in FIGS. 1 and 2. All particleboard mats were prepressed for ease of handling. The platens 1 and 2 each had dimensions of 24 X 24 X 2 /1; inches. Passageways 8 and 9 were formed 3 inches apart, /2 inch from each platens inner surface. The apertures 6 and 7 were spaced 2 /2 inches along the passageways 8 and 9 respectively. Asbestos gaskets 23 and 24 were placed between the platens l and 2 and the sealing frame member 3 to enable the chamber 4 to maintain steam pressures of at least 300 psi with a press force of approximately 150 tons. When the desired steam pressure was reached within the chamber 4 the outlet valve 18 was opened to allow steam flow of about 0.4 to 0.5 lb. per minute while maintaining the pressure within 2 percent. After the desired steam time had elapsed the inlet valve was shut off and the exhaust valves opened to release the pressure in the chamber and the mat. The release time was normally less than 30 seconds. The indicated "press time" refers to the time for the whole press cycle from the time the press was loaded until opened. Steam-time indicates the duration of steam flow through the mat. Platen temperature was maintained above the steam temperature to prevent condensation. Steam-pressing refers to the pressing method according to the present invention while conventional pressing refers to pressing without the use of steam injection.

EXAMPLE 1 Wood of two species. poplar (Populus grandidentata Michx) and sugar maple (Acer saccharum Marsh) was cut into flakes or made into splinters by hammermilling veneer. All the tlakes and splinters had a moisture content between 6 and 9 percent before resin application.

A commercially available. liquid phenolformaldehyde resin containing 43 percent solids at pH 1 1.6 to 11.9 was used for all boards. It was sprayed on in a laboratory rotating drum blender.

No paraffin was used in any of the boards.

Three types of board were made: a homogeneous board (splinters-Vs to A inches screened, with 4 percent resin content); flakeboard (flakes-0.035 X 1 Va X A to 2 inches, with 5 percent resin content); and a three-layer board made with fine splinters (1/16 inches screened, with 8 percent resin content) on face layers and coarse splinters (Vs to A inches screened with 6 percent resin content in the core).

The pressed board was weighed immediately and then cut in half. Each half was weighed again and its thickness measured. One half was immediately placed in an oven for a 16-hour post-cure at 220F and ovendry weight determination. The other half was conditioned to equilibrium at 70F and percent relative humidity. The same conditioning was given to the postcured halves before testing. Density was calculated on the basis of oven-dry weight and conditioned volume.

Torsion-shear strength was measured on l-inch square specimens, systematically sampled from each half board. The normal torsion-shear strength was obtained from ten specimens which were tested dry. The wet torsion-shear strength was measured on another ten specimens which had been subjected to an accelerated aging treatment (2-hour immersion in boiling water) and were tested wet.

All the torsion-shear values reported are averages of ten measurements made at the centre plane. The internal bond strength in psi is about 1 1.3 times the torsionshear value in ft-lb for a 1-inch square specimen.

Thickness expansion and water absorption tests PRESS MOISTURE THICK- STEAM TIME OARD CONTENT FAILING NESS WATER PRES- STEAM PLATEN 1 STEAM H1CK- DEN- (HOT TORQUE EXPAN- Aparslglg- OARD TYPE SURE TEMP. TEMP. TIME] NESS SITY BOARD) (ft-1b.) SION THICKNESS (psig) (F) (F) (min.) (in.) (pcf) DRY WET MAPLE SPLINTERS 200 388 400 2 11] 0.949 44.7 12.4 12.9 4.4 10.0 60.3 0 38B 400 3 [2] 0.929 45.7 13.4 13.5 4.6 10.8 59.0 1 Inch 280 388 400 4 [3] 0.903 45.8 11.6 13.0 5.3 9.2 56.6 200 388 400 S [4] 0.894 45.9 13.0 13.5 5.1 12.0 53.9 200 388 400 6 [5] 0.900 45.9 13.5 12.6 4.9 9.1 57.9 200 388 400 8 [7] 0.891 46.4 12.1 13.6 5.7 9.0 55.3 200 388 400 10 [9| 0.889 44.6 11.6 11.5 4.7 8.4 57.3 260 410 415 3 [2} 0.924 56.8 13.1 21.0 8.7 9.6 38.4 (CONVENTIONAL 400 20 0.984 40.9 2.1 10.8 4.5 23.4 89.2 PRESS) 400 25 0.981 41.0 1.5 13.6 5.2 23.5 90.5 400 30 0.933 43.2 1.2 1 1.5 4.3 24.4 89.5 400 20 0.984 47.0 3.2 13.0 2.3 34.4 83.5

-Continued PRESS MOISTURE THICK- STEAM TIME OARD CONTENT FAILING NESS WATER PRES- STEAM PLATEN (STEAM HlCK- DEN- (HOT TORQUE EXPAN- ABSOR- BOARD TYPE SURE TEMP. TEMP. TIME 1 NESS SlTY BOARD) (ft-lb.) SION PTION & THICKNESS (psig) 1F) 1F) (min.) (111.) (p f) DRY WET 1%) 1%) 400 0.986 45.2 2.4 12.6 2.6 34.0 89.0 400 0.985 44.2 1.9 14.0 2.9 32.0 88.8 400 20 0.986 53.1 4.2 24.8 4.1 42.9 79.6 2 inch 200 388 400 2 1161 2.014 47.3 9.6 15.1 3.2 11.1 54.4 225 396 405 5 131 1.953 42.7 10.1 11.2 4.9 10.8 55.6 225 396 405 5 131 1.950 42.5 10.6 11.2 4.7 11.0 60.0 225 396 405 5 13) 1.952 42.5 10.5 11.4 4.9 10.1 58.3 250 405 415 2 111 1.986 47.3 9.7 16.8 5.3 8.9 51.3 CONVENTIONAL 400 50 2.013 47.6 6.2 16.9 0.0 56.6 94.6 PRESS) S-inch 200 388 400 11 4 4.894 45.6 15.8 14.2 5.2 9.7 57.6 MAPLE FLAKES 200 388 400 6 [3 1.967 43.0 10.6 15.8 4.7 9.2 57.6 Z-inch 225 396 400 6 31 1.962 42.1 10.0 12.7 4.9 9.0 54.2 POPLAR FLAKES 150 367 380 5 13 1.945 41.0 14.0 7.5 3.6 11 7 58.0 2-inch 150 367 380 5 131 1.875 37.1 15.1 6.2 2.0 11.3 68.7 150 367 380 5 [3] 1.856 35.7 14.7 5.4 2.9 10.5 72.6 200 388 400 7 141 L843 45.2 14.2 8.6 3.9 9.4 57.2 200 388 400 7 141 1.845 45.3 14.0 8.6 3.7 9.6 56.7 3-lflCh 225 396 405 7 151 2.895 35.5 15.2 4.6 2.7 7.6 67.1 225 405 405 7 [5] 2.875 37.5 14.7 4.9 2.9 9.8 58.5 225 396 405 5 3] 2.965 35.9 14.2 4.5 2.5 15.2 80.0 120 350 380 7 5] 2.902 38.5 14.6 6.0 1.3 13.1 82.5

POPLAR SPLINTERS (THREE-LAYER) 2-inch 200 388 400 5 [31 1.897 37.5 13.6 4.3 2.1 11.7 57.3 3-inch 225 396 405 7 [51 2.886 36.6 15.0 4.3 1.9 10.2 57.8

were carried out on l-inch square specimens from both the post-cured and control half of each board. For l-inch thick board, ten specimens were placed face to face with their upper edge 1 inch below water level. The water temperature was kept within 2 of 70F during the 24-hour soaking period. Thickness and weight increase were recorded on a percent of original basis at l. 2. 4, 6, and 24 hours.

The table indicates that the dry torsion-shear strengths were generally the same for steam-pressed and conventionally pressed board, but the wet torsionshear strengths were higher for steam-pressed board after the accelerated aging treatment referred to above. The steam-pressed board showed substantial improvement of dimensional stability. Both thickness expansion and water absorption were reduced.

The series of 7 l-inch maple boards show the effect of steaming time at 200 psi. In general board quality was not significiantly improved by prolonging the steam time.

EXAMPLE 2 About 28 lb. of hammer milled hard maple particles l/l6, mesh size) were sprayed with a commercial liquid phenol-formaldehyde resin (4 percent solid resin based on oven dry particle weight), and measured into 6 lb. batches, and each batch was formed and prepressed into a l /2 inch mat. A series of l-inch boards (43-48 pcf density) was made from these mats at satu- 30 rated steam pressures varying from 50 to 300 psi with two different steaming times (A and 3 min.).

It is evident that the highest steam pressure (300 psi, 423F) combined with a 3-min. steam time. produced the board having the least thickness expansion. The same steam pressure combined with a r-min.

steam time resulted in the board having the highest torsion-shear strength. It appeared that a higher steam pressure or a longer steam time would further reduce the thickness expansion but at the expense of torsionshear strength. This was confirmed by one board,

EXAMPLE 3 Hammer milled spruce particles (A-H20 mesh size) were sprayed with a commercial liquid ureaformaldehyde resin 10 percent solid resin on oven dry particle weight). Several batches of this material. each 5.7 lb 10 percent moisture content) were formed into STEAM-PRESS CONDITIONS STEAM STEAM PLATEN STEAM FAILINO TORQUE THICKNESS WATER PRESSURE TEMP. TEMP. TIME THICKNESS DENSITY (fL-lb.) EXPANSION ABSORPTION (psig) ("F) (*F.) (min.) (in) (Pcf) DRY WET (36) 1% 15 X 15-inch mats. The mats were prepressed at 150 psi pressure to consolidate the mat to l inch thick for easy handling. The prepressed mats were steampressed into 1 inch thick boards at various steam pressures with different press and steaming time as shown 5 sealing frame with allowance for springback which is in the following table. However the press close time (A dephhdaht the p y p p r ie f he mat and min. steam release time 1 min. and platen temperathe P ing H i i n. ture (350F) were constant. Torsion-shear strength and The present invention is not to be limited to thickness thickness expansion for steamed-pressed boards and of5 inches or less but appears to be equally applicable one conventionally-pressed board are also shown. to thickness of greater than 5 inches.

Thick- Steam Press ness Temp. Time Torsion- Expan- Steam [Platen [Steam Pressure Temp. Time] Density Shear sion (psi) "F tmin.) (pcf) (ft-lb) Steam Pressed 1 30 269 3 [1 1&1 40.3 12.6 3.2 2 50 297 3 [1 /1] 42.0 13.0 7.0 3 100 33s 2 /2] 40.3 11.2 7.9 4 100 338 3 [1 A1 42.1 12.6 5.8 5 100 338 5 [3 1s] 42.6 1.8 (delaminated) Conventionally Pressed 6 (350! 43.3 12.7 [6.1

It was further found that there was a significant dif- It will be understood that the present process is not ference in springback (permanent swelling after the limited to the use of the apparatus described herein. specimen had been boiled in water for 2 hours and reh i l im i I conditioned to reach equilibrium at 70F and 65 per- 1. A process for pressing particleboard in a press incent relative humidit b w steampressed d cludmg a pair of platens wherein each platen has aperconventionally-pressed b d Th i b k f tures opening to one surface thereof which is adjacent steam-pressed poplar flake-b d was f d 1 b 2 to to the other platen and chamber defining means enclos- 5 percent while for conventionally pressed boards it g the region between Said P mpri ing the was 2! to 33 percent. steps of:

Ths moisture content of steam-pressed boards was compressing a mat p ing wood particles and found to be reduced by l to 2 percent from an i iti l 35 a thermosettmg adheslve binder between sa1d platmoisture content ranging from 1 l to 14 percent. Lower h to deslred particleboard thlQkhess; steam pressure or a longer steam time tended to prolhlmduhmg Steam under Pressure the duce boards with lower moisture content than did Pf h through the apertures of one P higher steam pressure or a shorter steam time. [t was wlth Suffic'em Pressure to P through the mat also found that thick boards had higher moisture con- 40 from ohe Surface thereof to the other Suffaw tents than thin boards and that flakeboards had higher thereof and exhausting the Steam tlhmugh the P moisture contents than homogeneous boards after tures of other P resh'lchhg the exhaust Steam pressing rate to provide an elevated and substantially uni- The optimum steam time for proper curing is deterform Pressure temherawre cohdlhoh with!" mined partly by the porosity of the particleboard and thg chamber whlle Steam Passed through the "l also the nature of the thermosetting adhesive binder. It f length of shfficleht to Cure the adhesive was found that a less porous mat required longer steamand time and/or higher steam-pressure. Porosity is depenreleaslhg the gleam P from the chamb'ihafld dent on the wood particle configuration and board den- Separahhg the P for removal of the p sity. For example, flakeboard is less porous than a ho- I mogcneous splinter board of the same wood species h Pf of clalm l Wherelh the PR358 platens and density are mamtamed at a temperature at least equal to that Press time is shortened by increasing steam temperai i f l l h h t f th ture, pressure and steam flow rate through the mat. process 0 mm W erem, mg 0 e For the laborator regs med it was found that for steam is delayed until the pressure wtthm sa1d chamber 1 h h g d k i d th 1 I defining means reaches a predetermined magnitude. 2 2 e d e F fi g 4. The process of claim 1 wherein the direction of sizmp 1ot1;1 (5r thets (Zing-press process was 1n t e olrl etrI Steam flow is raversdi g j g fi g fl sg z m w m 5. The process of claim 1 wherein said mat is preressed nor to bem ressed between sa1d latenst It will be understood that other means for mamtamp p g p p 

1. A PROCESS FOR PRESSING PARTICLEBOARD IN A PRESS INCLUDING A PAIR OF PLATEN WHEREIN EACH PLATEN HAS APERTURES OPENING TO ONE SURFACE THEREOF WHICH IS ADJACENT TO THE OTHER PLATEN AND CHAMBER DEFINING MEANS ENCLOSING THE REGION BETWEEN SAID PLATENS, COMPRISING THE STEPS OF: A. COMPRESSING A MAT COMPRISING WOOD PARTICLES AND A THERMOSETTING ADHESIVE BINDER BETWEEN SAID PLATENS TO THE DESIRED PARTICLEBOARD THICKNESS, B. INTRODUCING STEAM UNDER PRESSURE INTO THE COMPRESSED MAT THROUGH THE APERTURES OF ONE PLATEN WITH SUFFICIENT PRESSURE TO PASS THROUGH THE MAT FROM ONE SURFACE THEREOF TO THE OTHER SURFACE THEREOF, AND EXHAUSITING THE STEAM THROUGH THE APERTURES OF THE OTHER PLATEN RESTRICTING THE EXHAUSTS RATE TO PROVIDE AN ELEVATED AND SUBSTANTIALLY UNIFORM PRESSURE AND TEMPERATURE CONDITION WITHIN THE CHAMBER WHILE STEAM IS PASSED THROUGH THE MAT, FOR A LENGTH OF TIME SUFFICIENT TO CURE THE ADHESIVE BINDER; AND C. RELEASING THE STEAM PRESSURE FROM THE CHAMBER AND SEPARATING THE PLATENS FOR REMOVAL OF THE PARTICLEBOARD.
 2. The process of claim 1 wherein the press platens are maintained at a temperature at least equal to that of the steam.
 3. The process of claim 1 wherein exhausting of the steam is delayed until the pressure within said chamber defining means reaches a predetermined magnitude.
 4. The process of claim 1 wherein the direction of steam flow is reversed.
 5. The process of claim 1 wherein said mat is prepressed prior to being pressed between said platens. 